Comco PETP
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Comco-Plastic GmbH |
| Trademark: | Comco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9KobKD_Comco-PETP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Comco PETP is a Polyethylene Terephthalate (PET) material. It is available in Europe. Primary attribute of Comco PETP: Flame Rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Water Absorption | |||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | % | |
| Water Absorption | ISO 62 | ||
| after 24 h immersion in water : 23°C | 6.0 | mg | |
| after 96 h immersion in water : 23°C | 13.0 | mg |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | |||
| in air continuosly | 115 | °C | |
| in air for short periods | 160 | °C | |
| Service Temperature - Minimum | -20 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 96 | ISO 2039-2 | |
| Ball Indentation Hardness | 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3700 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 15 | % | ISO 527-2 |
| Tensile Creep Modulus 1(1000 hr) | 26.0 | MPa | ISO 899-1 |
| Compressive Stress | ISO 604 | ||
| 5% Strain | 103 | MPa | |
| 2% Strain | 51.0 | MPa | |
| 1% Strain | 26.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | > 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 2.0 | kJ/m² | ISO 180/2A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/A |
| Melting Temperature | 255 | °C | |
| CLTE - Flow | |||
| 23 to 60°C | 6.0E-5 | cm/cm/°C | |
| 23 to 100°C | 8.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.29 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.40 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 0.014 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 6.00 mm | HB | ||
| Oxygen Index | 25 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 1% Strain |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S ESL128 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Toyolac® AX05 X03 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Wondel® T PETG6 | Nanjing Julong Engineering Plastics Co., LTD | PET | Wondel® T |
| Elastron® G G300.A57.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Sylvin 8950-70FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |