COSMOPLENE® FL7320L
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9KWBvg_COSMOPLENE-FL7320L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOPLENE FL7320L is Polypropylene Terpolymer product with better Aluminum adhesiveness, higher heat resistance and good wetting tension retention after corona treatment. COSMOPLENE FL7320L is designed for Aluminum metalized cast film (M-CPP) application. FL7320L contains antiblocking agent only. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 870 | % | ASTM D638 |
| Apparent Bending Modulus | 1200 | MPa | ASTM D747 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | Internal Method | ||
| MD : 30 µm | 690 | MPa | |
| TD : 30 µm | 710 | MPa | |
| Seal Initiation Temperature (30 µm) | 130 | °C | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 146 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (30.0 µm) | 165 | ASTM D2457 | |
| Haze (30.0 µm) | 2.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 | °C | |
| Take-Off Roll | 26.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PTFE DISP 40 | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| King Pearl® G-H | Loyal Chemical | PS (EPS) | King Pearl® |
| Karina IVORY PVC COMPOUND -E 602D35/ 1-A-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LinGen FR180 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PPE | LinGen |
| TECACOMP® PEEK LDS black 3980 | Ensinger GmbH | PEEK | TECACOMP® |