TECHNYL STAR™ A 205 F NATURAL S
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL STAR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9HkPx4_TECHNYL-STAR-A-205-F-NATURAL-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYLSTAR A205 F NATURAL S is a polyamide 6.6 with low viscosity for fast cycle moulding. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.15 | -- | g/cm³ | ASTM D792 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3300 | 2270 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 80.0 | 79.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 32 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3070 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.4 | 6.6 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179 | |
| Notched Izod Impact Strength (23°C) | 3.5 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 153 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 69.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 262 | -- | °C | ASTM D3418 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (23°C) | 27 | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C, 1 MHz) | 2.90 | 3.20 | IEC 60250 | |
| Dissipation Factor (23°C, 1 MHz) | 0.030 | 0.080 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 285 | °C | |
| Front Temperature | 270 to 285 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPC343T4 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| TAROLOX 111 G9 | Taro Plast S.p.A. | PET | TAROLOX |
| BUP 690 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| ARC ARC5009 | ARC Resin Corporation | Acetal (POM) Copolymer | ARC |
| LNP™ LUBRICOMP™ KA000M compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |