Hanwha Total PP SH53C
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Gk92e_Hanwha-Total-PP-SH53C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SH53C is a polypropylene that displays improved heat resistance and dimensional stability when compared to other high gloss PP brands. Often, other high gloss brands have the gloss but a much lower resistance to thermal strain, unsuitable for use in electric heating equipment. This grade is popularly used in high-temperature electric heating equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.0 - 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 35.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 15 | % | ASTM D638 |
| Flexural Modulus 3 | 3330 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 41 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 142 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 180 - 210 | °C | |
| Nozzle Temperature | 180 - 210 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Pressure | 39.2 - 68.6 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa |
| Injection instructions |
|---|
| Injection Speed: 40 to 70 % |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYFLUOR® 860 | Greene, Tweed & Co. | Fluorelastomer | XYFLUOR® |
| Celanex® 3316HR | Celanese Corporation | PBT | Celanex® |
| DIAMALOY ABSPC 9902 LM 1402 Black | Network Polymers, Inc. | PC+ABS | DIAMALOY ABSPC |
| PHOENIX™ 11101 | Phon Tech Industrial Company | SBC | PHOENIX™ |
| Sylvin 83013-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |