CYCOLOY™ C2800 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9GXQiz_CYCOLOY-C2800-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-chlorinated and non-brominated flame retardant PC+ABS offering balanced flow and impact properties for various applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.17 | g/cm³ | |
| -- 1 | 1.18 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | |
| Equilibrium, 23°C | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2690 | MPa | ASTM D638 |
| Tensile Strength 3(Yield) | 58.6 | MPa | ASTM D638 |
| Tensile Elongation 4 | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 50 | % | |
| Flexural Modulus 5(100 mm Span) | 2690 | MPa | ASTM D790 |
| Flexural Strength 6(Yield, 100 mm Span) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 430 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 58.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 73.9 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 80.0 | °C | |
| Vicat Softening Temperature | 90.6 | °C | ASTM D1525 7 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 60°C | 7.2E-5 | cm/cm/°C | |
| Transverse : -40 to 60°C | 7.2E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 70.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.00 | ||
| 60 Hz | 3.00 | ||
| 100 Hz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 4.8E-3 | ||
| 60 Hz | 4.8E-3 | ||
| Arc Resistance 8 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.889 mm | V-2 | ||
| 1.47 mm | V-0 | ||
| 2.31 mm | 5VB | ||
| Oxygen Index | 35 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 77.0 to 82.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 210 to 254 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 227 to 274 | °C | |
| Nozzle Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 49.0 to 71.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Color |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| 8 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 121-79W233 | ExxonMobil Chemical | TPV | Santoprene™ |
| Shanghai Potomer SG7 | Shanghai Potomer International Trade Co., Ltd. | PVC, Rigid | Shanghai Potomer |
| NuSil MED-4120 | NuSil Technology | Rubber | NuSil |
| Beetafin® L9086 | BIP (Oldbury) Limited | PUR-Ester | Beetafin® |
| Chiao Fu PP PP212GM30 NAT | Chiao Fu Enterprises Co., Ltd. | PP, Unspecified | Chiao Fu PP |