Ultramid® 8202C HS BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9GIKcp_Ultramid-8202C-HS-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8202C HS BK-102 is a heat stabilized, low viscosity, pigmented black, PA6, injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in non-heat stabilized (Ultramid 8202C). Applications Ultramid 8202C HS BK-102 is generally recommended for applications such as gears, valves, fittings, insulators, bushings, slides, window hardware, wiring devices, textile components and furniture casters. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.6 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.6 | -- | % | ISO 62 |
| Saturation | 9.3 | -- | % | ASTM D570 |
| Saturation, 23°C | 9.3 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.6 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 | |
| Ball Indentation Hardness | 200 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3500 | 1360 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Yield, -40°C | 137 | 142 | MPa | ASTM D638 |
| Yield, 23°C | 90.0 | 48.0 | MPa | ASTM D638 |
| Yield, 80°C | 40.0 | 30.0 | MPa | ASTM D638 |
| Yield, 121°C | 30.0 | 25.0 | MPa | ASTM D638 |
| Yield, 23°C | 85.0 | 43.0 | MPa | ISO 527-2 |
| Break, -40°C | 130 | 80.0 | MPa | ASTM D638 |
| Break, 23°C | 90.0 | 70.0 | MPa | ASTM D638 |
| Break, 80°C | 35.0 | 30.0 | MPa | ASTM D638 |
| Break, 121°C | 25.0 | 20.0 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield, -40°C | 3.0 | 3.0 | % | ASTM D638 |
| Yield, 23°C | 4.0 | 22 | % | ASTM D638, ISO 527-2 |
| Yield, 80°C | 25 | 25 | % | ASTM D638 |
| Yield, 121°C | 27 | 30 | % | ASTM D638 |
| Break, -40°C | 5.0 | 3.0 | % | ASTM D638 |
| Break, 23°C | 12 | > 100 | % | ASTM D638 |
| Break, 80°C | > 100 | > 100 | % | ASTM D638 |
| Break, 121°C | > 100 | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 10 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -40°C | 3370 | 4200 | MPa | ASTM D790 |
| 23°C | 3170 | 970 | MPa | ASTM D790 |
| 65°C | 600 | -- | MPa | ASTM D790 |
| 90°C | 440 | -- | MPa | ASTM D790 |
| 121°C | 385 | -- | MPa | ASTM D790 |
| 23°C | 2800 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| -40°C | 183 | 168 | MPa | ASTM D790 |
| 23°C | 110 | 42.0 | MPa | ASTM D790 |
| 65°C | 30.0 | -- | MPa | ASTM D790 |
| 121°C | 21.0 | -- | MPa | ASTM D790 |
| 23°C | 95.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179 | |
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 32 | 21 | J/m | |
| 23°C | 48 | 170 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 190 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 8.1E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| 6.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| 6.00 mm | V-2 | -- |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Drop Weight Impact Strength (23°C) | 122 | > 271 | J | Internal Method |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMALGRAPH® EWC-600X | Cytec Industries Inc. | Carbon/Epoxy | THERMALGRAPH® |
| Yuyao PC PC303 | Yuyao Tenglong Plastics Co., Ltd. | PC | Yuyao PC |
| ADEKA PR series | Adeka Corporation | PUR-Ether | ADEKA |
| Ferro PP MPP20FU16BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Geon™ Vinyl Rigid Extrusion L9620 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |