Network Polymers PC 1900 is a Polycarbonate (PC) product. It is available in North America. |
General Information |
---|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) 1(300°C/1.2 kg) | 19 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength 2(Yield) | 64.1 | MPa | ASTM D638 |
Flexural Modulus 3 | 2350 | MPa | ASTM D790B |
Flexural Strength 4(5.0% Strain) | 93.1 | MPa | ASTM D790B |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (3.18 mm) | 800 | J/m | ASTM D256A |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 128 | °C | ASTM D648 |
Note Message | |
---|---|
1 . | Procedure A |
2 . | 51 mm/min |
3 . | Method I (3 point load), 1.3 mm/min |
4 . | Method I (3 point load), 1.3 mm/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RTP 200 A TC-I-10 | RTP Company | Nylon 6 | RTP |
Xuchuan XCA-4050 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
Latimass 62-07 D025 | LATI S.p.A. | Nylon 6 | Latimass |
Karina YELLOW PVC COMPOUND -E 780-02/167-A-IS (C800) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
Hostacom EKC 265N/2 D8V689 | LyondellBasell Industries | PP Copolymer | Hostacom |