Alathon® M5352
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9EKdb3_Alathon-M5352.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Alathon M5352 is a copolymer with narrow molecular weight distribution. This resin provides high impact strength and stress crack resistance, excellent color, low odor and good processing stability. Typical applications include open head pails, large shipping containers and 55-gallon drum lids. M5352 meets the requirements of the Food and Drug Administration regulation 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 - 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Spiral Flow | 19.8 | cm | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- 2 | 897 | MPa | ASTM D638 |
| 1% secant | 727 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 3 | 27.6 | MPa | ASTM D638 |
| Fracture 4 | 27.6 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield 5 | 11 | % | ASTM D638 |
| Fracture 6 | 1700 | % | ASTM D638 |
| Flexural Modulus 7 | ASTM D790 | ||
| -- 8 | 1290 | MPa | ASTM D790 |
| 1% secant | 1190 | MPa | ASTM D790 |
| 2% secant | 978 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 73.1 | °C | ASTM D648 |
| Brittleness Temperature 9 | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Melting Temperature | 131 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 116 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C | |
| Processing (Melt) Temp | 246 - 280 | °C | |
| Mold Temperature | 7.00 - 18.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Pressure: Maximum (w/out flash)Holding Pressure: Minimum (75 to 85% of Injection Pressure)Cushion: Minimum but presentDecompression Range: 0.25 to 0.50 in |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Tensile Young's Modulus |
| 3 . | Type 4, 50mm/min |
| 4 . | 50 mm/min |
| 5 . | Type 4, 50mm/min |
| 6 . | 50 mm/min |
| 7 . | 13 mm/min |
| 8 . | Flexural Young's Modulus |
| 9 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DURAFIDE® 6465A6 | Polyplastics Co., Ltd. | PPS | DURAFIDE® |
| KIBISAN® PN-127 | CHI MEI CORPORATION | SAN | KIBISAN® |
| Karina BEIGE COLOR CONCENTRATE -E 08/415-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lutene® H BE0350 | LG Chem Ltd. | HDPE | Lutene® H |
| Kinta FR5010G | Kinta Technology (Hong Kong) Co., Ltd. | PC | Kinta |