Generic ASA
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9E5Wft_Generic-ASA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ASA This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.06 - 1.07 | g/cm³ | ASTM D792 |
| 23°C | 1.04 - 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 2.5 - 18 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 3.4 - 26 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 3.80 - 20.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.50 - 0.61 | % | ASTM D955 |
| 23°C | 0.50 - 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.25 - 0.35 | % | ASTM D570 |
| 23°C, 24 hr | 0.30 | % | ISO 62 |
| Saturated, 23°C | 0.50 - 1.7 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.19 - 0.37 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 85 - 110 | ASTM D785 | |
| 23°C | 82 - 114 | ISO 2039-2 | |
| Ball Indentation Hardness | 65.0 - 105 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1700 - 2590 | MPa | ASTM D638 |
| 23°C | 1730 - 2720 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 34.7 - 50.2 | MPa | ASTM D638 |
| Yield, 23°C | 36.4 - 55.6 | MPa | ISO 527-2 |
| Fracture, 23°C | 29.9 - 56.8 | MPa | ASTM D638 |
| Fracture, 23°C | 28.7 - 62.0 | MPa | ISO 527-2 |
| 23°C | 39.7 - 50.9 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.7 - 6.1 | % | ASTM D638 |
| Yield, 23°C | 2.9 - 6.0 | % | ISO 527-2 |
| Fracture, 23°C | 14 - 100 | % | ASTM D638 |
| Fracture, 23°C | 3.0 - 53 | % | ISO 527-2 |
| Tensile Creep Modulus (1000 hr) | 1250 | MPa | ISO 899-1 |
| Flexural Modulus | |||
| 23°C | 1760 - 2470 | MPa | ASTM D790 |
| 23°C | 1850 - 2930 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 51.4 - 79.0 | MPa | ASTM D790 |
| 23°C | 52.2 - 80.1 | MPa | ISO 178 |
| Yield, 23°C | 52.9 - 85.0 | MPa | ASTM D790 |
| Fracture, 23°C | 52.0 - 70.0 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break, 23°C) | 8.0 - 12 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 - 19 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 24 - 100 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 52 - 410 | J/m | ASTM D256 |
| 23°C | 6.5 - 26 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 3.72 - 35.7 | J | ASTM D3763 |
| Dart Drop Impact (23°C) | 24.8 - 25.5 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 86.7 - 107 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 83.9 - 104 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 98.8 - 106 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 76.5 - 103 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 74.5 - 97.6 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 94.9 - 95.9 | °C | ASTM D648 |
| 1.8 MPa, annealed | 88.0 - 103 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 92.0 - 107 | °C | ASTM D1525 |
| -- | 89.6 - 108 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 8.5E-5 - 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 8.4E-5 - 9.0E-5 | cm/cm/°C | ASTM E831 |
| Flow | 6.9E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 9.2E-5 - 9.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 8.7E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.17 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 15 - 1.0E+15 | ohms·cm | ASTM D257 |
| 23°C | 7.6E+13 - 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 16 - 18 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 23°C | 3.04 - 5.20 | ASTM D150 | |
| 23°C | 3.69 - 3.90 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.025 - 0.15 | ASTM D150 | |
| 23°C | 9.0E-3 - 0.035 | IEC 60250 | |
| Comparative Tracking Index | 589 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 - 751 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 550 - 651 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | 19 - 97 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 - 95.1 | °C | |
| Drying Time | 2.9 - 4.0 | hr | |
| Suggested Max Moisture | 0.039 - 0.20 | % | |
| Suggested Shot Size | 55 - 60 | % | |
| Suggested Max Regrind | 18 | % | |
| Rear Temperature | 188 - 251 | °C | |
| Middle Temperature | 198 - 250 | °C | |
| Front Temperature | 225 - 256 | °C | |
| Nozzle Temperature | 215 - 261 | °C | |
| Processing (Melt) Temp | 215 - 260 | °C | |
| Mold Temperature | 60.0 - 60.7 | °C | |
| Injection Pressure | 67.8 - 105 | MPa | |
| Back Pressure | 0.300 - 10.1 | MPa | |
| Screw Speed | 49 - 76 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ASAThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.9 - 88.1 | °C | |
| Drying Time | 2.5 - 4.5 | hr | |
| Suggested Max Moisture | 0.010 - 0.051 | % | |
| Cylinder Zone 1 Temp. | 180 - 210 | °C | |
| Cylinder Zone 2 Temp. | 188 - 224 | °C | |
| Cylinder Zone 3 Temp. | 188 - 230 | °C | |
| Cylinder Zone 4 Temp. | 188 - 235 | °C | |
| Cylinder Zone 5 Temp. | 188 - 206 | °C | |
| Adapter Temperature | 204 - 235 | °C | |
| Melt Temperature | 215 - 245 | °C | |
| Die Temperature | 200 - 235 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ASAThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E190 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Witcom PP 2012/078 Blue | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| XYRON™ X531V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Generic Nylon 11 | Generic | Nylon 11 | Generic |
| ALCOM® PA66 910/1.1 CF15 GF20 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |