SCHULAKETON GF 15
| Category: | PK-Aliphatic , Polyketone, Aliphatic |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAKETON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Dkam9_SCHULAKETON-GF-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% glass fiber reinforced aliphatic Polyketon |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (240°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | |||
| -40°C | 50 | kJ/m² | ISO 179 |
| 23°C | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 207 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang WM-7508S | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| EL-Lene™ M735RU | SCG Chemicals Co., Ltd. | LLDPE | EL-Lene™ |
| INSULCAST® 502/INSULCURE 9 | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| Durez® 51010 | SBHPP | Phenolic | Durez® |
| CERTENE™ PBM-2NB | Muehlstein | PP Impact Copolymer | CERTENE™ |