Pebax® Rnew 72R53 SP 01
| Category: | PEBA-Ether , Polyether Block Amide |
| Manufacturer: | Arkema |
| Trademark: | Pebax® Rnew |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9DHZ3x_Pebax-Rnew-72R53-SP-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyether block amide Pebax® Rnew 72R53 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | Internal Method | ||
| Across Flow : 24 hr, 4.00 mm | 1.3 | % | |
| Flow : 24 hr, 4.00 mm | 1.5 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.70 | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 2 | ISO 868 | ||
| Shore D | 71 | ||
| Shore D, 15 sec | 65 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3(Break) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain 4(Break) | > 300 | % | ISO 527-2 |
| Flexural Modulus 5 | 560 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 175 | °C | ISO 306 |
| Melting Temperature | 186 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | 93 to 97 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 5.0 to 7.0 | hr | |
| Processing (Melt) Temp | 230 to 290 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 5.0 to 7.0 | hr | |
| Melt Temperature | 230 to 290 | °C |
| Note Message | |
|---|---|
| 1 . | Mold at 40°C |
| 2 . | Samples conditioned 15 days at 23°C - 50 % R.H |
| 3 . | Samples conditioned 15 days at 23°C - 50 % R.H |
| 4 . | Samples conditioned 15 days at 23°C - 50 % R.H |
| 5 . | Samples conditioned 15 days at 23°C - 50 % R.H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 3554 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Nymax™ 1200 HR NC088 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Evoprene™ LF 6154 | AlphaGary | SBC | Evoprene™ LF |
| Fiberfil® J-68/20/E/SD | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| Hostaform® C 9021 GV1/10 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |