KOPLA PA66 KDT1020
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 99lsIW_KOPLA-PA66-KDT1020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA66 KDT1020 is a Polyamide 66 (Nylon 66) material filled with mineral. It is available in Asia Pacific. Important attributes of KOPLA PA66 KDT1020 are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 73.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4120 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 240 | °C | |
| 1.8 MPa, Unannealed | 225 | °C | |
| Melting Temperature | 260 | °C | |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 305 TFE 15 SI 2 HB | RTP Company | PC | RTP |
| SABIC® PC PC1003R resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| Sup-tech B705EX | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 6 | Sup-tech |
| Cheng Yu 3245 | Cheng Yu Plastic Company Limited | TPE | Cheng Yu |
| KRATON® G1654 H | Kraton Polymers LLC | SEBS | KRATON® |