TRIBOCOMP® PPA CF30 TS0
| Category: | PPA , Polyphthalamide |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 99C1vG_TRIBOCOMP-PPA-CF30-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® PPA CF30 TS0 is a Polyphthalamide (PPA) product filled with 30% carbon fiber. It is available in Europe. Primary characteristic: lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 23000 | 22500 | MPa | |
| 90°C | 21000 | -- | MPa | |
| 120°C | 16500 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 220 | 210 | MPa | |
| Yield, 90°C | 195 | -- | MPa | |
| Yield, 120°C | 150 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 2.0 | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 22000 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 335 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 40 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 300 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 285 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.1E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.52 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+2 | -- | ohms | ASTM D257 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 320 to 340 | °C | |
| Middle Temperature | 320 to 335 | °C | |
| Front Temperature | 320 to 335 | °C | |
| Nozzle Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | < 340 | °C | |
| Mold Temperature | 135 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 L Z | RTP Company | PC | RTP |
| APEX® 1500-65D | Teknor Apex Company | PVC, Flexible | APEX® |
| AURAPENE PPTF40 Black | Aurora Manufacturing Ltd | TPO | AURAPENE |
| Halene H E5201 | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| LNP™ THERMOTUF™ VX00585 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |