Capran® 1000 Datasheet,Nylon 6,Honeywell-SHANGHAI SUSHENG

Message
CAPRAN® 1000 is a 0.40 mil (10 micron) biaxially oriented nylon 6 film with excellent flex crack resistance and superior clarity properties well suited for packaging applications requiring excellent mechanical strength.

General Information
Features	High strength Good cracking resistance Definition, high
Uses	Bi-axially Oriented Film Packaging
Forms	Films

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With Metal-Dynamic	0.23	ASTM D1894
With self-dynamics	0.75	ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	10	µm
secant modulus			ASTM D882
MD : 10 µm	2760	MPa	ASTM D882
TD : 10 µm	2760	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Break, 100 µm	262	MPa	ASTM D882
TD : Break, 100 µm	262	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 100 µm	75	%	ASTM D882
TD : Break, 100 µm	75	%	ASTM D882
Oxygen Permeability (25°C, 100 µm)	1.7	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission Rate (10 µm, 38°C, 100% RH)	420	g·mm/m²/atm/24 hr	ASTM F1249

Optical	Nominal Value	Unit	Test Method
Gloss (20°, 102 µm)	160 - 180		ASTM D2457
Haze (102 µm)	1.7 - 3.0	%	ASTM D1003

Additional Information
Yield: 59800 in²/lbTensile Strength @ Break, ASTM D 882, MD: 34000 to 42000 psiTensile Strength @ Break, ASTM D 882, TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD: 60 to 90%Elongation @ Break, ASTM 882, TD: 60 to 90%Secant Modulus, ASTM D 882, MD: 350000 to 450000 psiSecant Modulus, ASTM D 882, TD: 350000 to 450000 psiGraves Tear (initial), ASTM D 1004, MD: 1100 to1500 g/milGraves Tear (initial), ASTM D 1004, TD: 1100 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 0.2 to 0.7% shrinkageWater Vapor Transmission ASTM F 1249, 100°F, 100%RH: 25 to 30 g/100 in²/dayOxygen Transmission Rate, ASTM D3985, 100°F, 100% RH: 25 to 30 g/100 in²/day

Additional Information

Yield: 59800 in²/lbTensile Strength @ Break, ASTM D 882, MD: 34000 to 42000 psiTensile Strength @ Break, ASTM D 882, TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD: 60 to 90%Elongation @ Break, ASTM 882, TD: 60 to 90%Secant Modulus, ASTM D 882, MD: 350000 to 450000 psiSecant Modulus, ASTM D 882, TD: 350000 to 450000 psiGraves Tear (initial), ASTM D 1004, MD: 1100 to1500 g/milGraves Tear (initial), ASTM D 1004, TD: 1100 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 0.2 to 0.7% shrinkageWater Vapor Transmission ASTM F 1249, 100°F, 100%RH: 25 to 30 g/100 in²/dayOxygen Transmission Rate, ASTM D3985, 100°F, 100% RH: 25 to 30 g/100 in²/day

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Honeywell
Trademark:	Capran®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	999ddI_Capran-1000.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TAISOX 8230	Formosa Plastics Corporation	HDPE	TAISOX
Topilene® J460F	Hyosung Corporation	PP Impact Copolymer	Topilene®
NYLOY® KF-0020N 6221W	Nytex Composites Co., Ltd.	Nylon, Unspecified	NYLOY®
Hyundai EP PA66 LD460	HYUNDAI EP Co., Ltd.	Nylon 66	Hyundai EP PA66
Hyundai EP PA6 LS130	HYUNDAI EP Co., Ltd.	Nylon 6	Hyundai EP PA6