Lutene® H BE0400
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lutene® H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 98cVm9_Lutene-H-BE0400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUTENE - H BE0400 is an excellent materials for blow-molded articles with high densityand rigidty. It has good flow chracteristics and impact resistance. Main Applications Blow molded containers with capacities ranging a few milliliters up to 20 liters, Sheet |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.12 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 25 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | 50.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 20°C) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Fracture, 20°C) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (20°C) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Melting Temperature | 134 | °C | DSC |
| Heat Deflection Temperature | 76 | °C | ASTM D648 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 - 185 | °C | |
| Cylinder Zone 3 Temp. | 175 - 195 | °C | |
| Cylinder Zone 5 Temp. | 180 - 200 | °C | |
| Adapter Temperature | 175 - 190 | °C | |
| Melt Temperature | 180 - 200 | °C | |
| Die Temperature | 160 - 190 | °C |
| Extrusion instructions |
|---|
| CrossHead temp: 165 to 195°CMold Temp: 5 to 40°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NITRIFLEX NP-3083 | NITRIFLEX | NBR | NITRIFLEX |
| 4MID® 9B22130 HUV | 4Plas | Nylon 6 | 4MID® |
| LUVOCOM® 19-7278 | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| WELLAMID Nylon 6600-PA66-GV 20 HWV0CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| OTECH CPE OTE8840-07 - Cable Jacket | OTECH Corporation | CPE | OTECH CPE |