Alkathene® XLF175
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 98KciF_Alkathene-XLF175.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
XLF175 is a low density polyethylene of medium density designed to meet the needs of the overwrap market. XLF175 is formulated with a BHT free antioxidant package. XLF175 is intended primarily for applications such as the overwrap of paper products. It is necessary to add suitable levels of additives, particularly slip, to meet the conversion needs of high speed overwrapping equipment. XLF175 is suitable for food contact applications and conforms to the requirements of the United States Food and Drug Administration CFR 21 177.1520, paragraph (c), item 2.1. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.40 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 30 µm | 270 | MPa | ASTM D882 |
| 2% secant, TD : 30 µm | 340 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm | 11.0 | MPa | ASTM D882 |
| TD : Yield, 30 µm | 14.0 | MPa | ASTM D882 |
| MD : Break, 30 µm | 23.0 | MPa | ASTM D882 |
| TD : Break, 30 µm | 16.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 280 | % | ASTM D882 |
| TD : Break, 30 µm | 790 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 55 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm | 340 | g | ASTM D1922 |
| TD : 30 µm | 150 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (30.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from blown film processed at a blow up ratio of 3.2:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marvel™ M3504DXP | SCG Chemicals Co., Ltd. | PE, Unspecified | Marvel™ |
| RTP 2202 LF TFE 15 | RTP Company | PEEK | RTP |
| UBESTA XPA 9055 X1 | UBE Engineering Plastics, S.A. | Nylon 12 Elast | UBESTA |
| HAIPLEN H50 T4 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Karina WHITE PVC COMPOUND -E TR-652D10/ 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |