LNP™ THERMOCOMP™ WC006 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 982W1v_LNP-THERMOCOMP-WC006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP WC006 is a compound based on PBT resin containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound WC-1006 Product reorder name: WC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 2.0 | % | ASTM D955 |
| Across Flow : 24 hr | 1.2 | % | ISO 294-4 |
| Flow : 24 hr | 0.23 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 20000 | MPa | ASTM D638 |
| -- | 20700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 159 | MPa | ASTM D638 |
| Yield | 158 | MPa | ISO 527-2 |
| Break | 159 | MPa | ASTM D638 |
| Break | 158 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.2 | % | ASTM D638 |
| Yield | 1.3 | % | ISO 527-2 |
| Break | 1.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 15200 | MPa | ASTM D790 |
| -- | 17000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 207 | MPa | ASTM D790 |
| -- | 219 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 460 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.40 | J | ASTM D3763 |
| -- | 2.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 223 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 211 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 209 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR WC 0587-21 BE1 RoHS | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| SABIC® PP 576S | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| APEX® 78-A447-H | Teknor Apex Company | PVC, Flexible | APEX® |
| Elastollan® LP 9286 | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| Hyundai EP PA66 LD610 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |