LNP™ FARADEX™ AS003 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 97PlGg_LNPFARADEXAS003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP FARADEX AS003 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. Also known as: LNP* FARADEX* Compound AS-1003 Product reorder name: AS003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| -- | 1.15 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.39 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.27 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3160 | MPa | ASTM D638 |
| -- | 2700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 42.1 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2 |
| Fracture | 39.3 | MPa | ASTM D638 |
| Fracture | 37.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.6 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2 |
| Fracture | 6.2 | % | ASTM D638 |
| Fracture | 2.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3050 | MPa | ASTM D790 |
| -- | 2800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 310 | J/m | ASTM D4812 |
| 23°C 3 | 18 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 15.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 96.7 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 93.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 88.3 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 78.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 9.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 | ohms·cm | ASTM D257 |
| Shielding Effectiveness (3.00 mm) | 50 - 65 | dB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Rear Temperature | 210 - 221 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 254 - 266 | °C | |
| Processing (Melt) Temp | 238 - 254 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Roechling SUSTAPEEK | Röchling Sustaplast SE & Co. KG | PEEK | Roechling |
| DISTRUMID 6 GF30 HI | Distrupol | Nylon 6 | DISTRUMID |
| EPO-TEK® OG146-178 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LNP™ STAT-KON™ DE003E compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |
| Durethan® BM 25 FN20 DUS013 000000 | LANXESS GmbH | Nylon 6 | Durethan® |