Multilon® R-2010
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Multilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 97DkLB_MultilonR2010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fiber reinforced PC/ABS polymer alloy, Automotive series |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Transverse flow : 4.00mm | 0.40 - 0.60 | % | Internal method |
| Flow : 4.00mm | 0.30 - 0.50 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3950 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 3800 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 10 | kJ/m² | ISO 179 |
| 23°C | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 137 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ 1000H | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Multi-Flex® TPE A8103 E | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| ISPLEN® PM 360 AT | REPSOL | PP Homopolymer | ISPLEN® |
| Lumid® HI1102A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |
| Hifax EKC 244X 1 BLACK | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |