SURPASS® FPs016-C
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SURPASS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 96lrtt_SURPASS-FPs016-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SURPASS® FPs016-C is a Linear Low Density Polyethylene material. It is available in North America for film extrusion. Important attributes of SURPASS® FPs016-C are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.65 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 126 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 138 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 8.50 | MPa | |
| TD : Yield, 25 µm, Blown Film | 8.50 | MPa | |
| MD : Break, 25 µm, Blown Film | 47.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 44.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 470 | % | |
| TD : Break, 25 µm, Blown Film | 780 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 700 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 350 | g | |
| TD : 25 µm, Blown Film | 430 | g | |
| Seal Initiation Temperature 1(25 µm, Blown Film) | 100 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 25.0 µm, Blown Film 2 | 72 | ||
| 45°, 25.0 µm, Blown Film 3 | 38 | ||
| Haze | ASTM D1003 | ||
| 25.0 µm, Blown Film 4 | 7.0 | % | |
| 25.0 µm, Blown Film 5 | 15 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Low Friction Puncture - Blown Film (25.0 µm) | 980 | J/cm |
| Note Message | |
|---|---|
| 1 . | Temperature at which a 2 mil film achieves a seal strength of 4.4N/13mm. 0.5 sec dwell, 0.27 N/mm² bar pressure, 305 mm/min pull speed |
| 2 . | LDPE Blended |
| 3 . | 100% LLDPE |
| 4 . | LDPE Blended |
| 5 . | 100% LLDPE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 TC-I-20 SE | RTP Company | PPS | RTP |
| SABIC® PPcompound 20MBT | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| ELEVATE™ EF526 | Westlake Chemical Corporation | EVA | ELEVATE™ |
| Glastic® 1580 | Glastic Corporation | Polyester, TS | Glastic® |
| LEXAN™ IR1810 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |