LNP™ STAT-LOY™ A30009 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 94XhSf_LNP-STAT-LOY-A30009-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY A30009 is a compound based on ABS. Added features of this material include: Antistatic, Flame Retardant. Also known as: LNP* STAT-LOY* Compound A-FR Product reorder name: A30009 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.80 to 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.88 | % | ISO 294-4 |
| Flow : 24 hr | 0.79 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 2.3 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 1720 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 32.4 | MPa | ASTM D638 |
| Yield | 32.0 | MPa | ISO 527-2 |
| Break | 24.1 | MPa | ASTM D638 |
| Break | 28.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.8 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2 |
| Break | 36 | % | ASTM D638 |
| Break | 15 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 41.4 | MPa | ASTM D790 |
| -- | 47.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1700 | J/m | ASTM D4812 |
| 23°C 3 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 14.7 | J | ASTM D3763 |
| -- | 4.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 95.6 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 94.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 81.1 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 81.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1935 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Geon™ Vinyl Flexible 90010 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Elvax® 150W | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Kuraray Poval® PVA 217 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| RTP 699 X 141368 B NS | RTP Company | ABS | RTP |