Fiberfil®J-68/10/E is a polypropylene copolymer (PP Copoly) material, which contains a 10% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main features of J-68/10/E are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.30 - 0.50 | % | ASTM D955 |
| 6.35 mm | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1650 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 33.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 9.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 1520 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 135 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 129 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L PA6 D36 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| Sylvin 9716-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Texalan® 3 Series 365A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| HONES® PBT GF10 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PBT | HONES® |
| LEXAN™ LUX7189 resin | SABIC Innovative Plastics | PC | LEXAN™ |