GELOY™ XTWE270M resin
| Category: | ASA+SAN , Acrylonitrile Styrene Acrylate + SAN |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 93Lf2a_GELOY-XTWE270M-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.7 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 2.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1910 | MPa | ASTM D638 |
| -- | 1790 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 36.0 | MPa | ASTM D638 |
| Yield | 36.0 | MPa | ISO 527-2/50 |
| Break 3 | 32.0 | MPa | ASTM D638 |
| Break | 26.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.4 | % | ASTM D638 |
| Yield | 3.4 | % | ISO 527-2/50 |
| Break 5 | 38 | % | ASTM D638 |
| Break | 28 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1830 | MPa | ASTM D790 |
| -- 7 | 1870 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 56.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 56.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 70 | J/m | ASTM D256 |
| 23°C | 200 | J/m | ASTM D256 |
| -30°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 13 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 28.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 69.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 71.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 85.0 | °C | ASTM D1525, ISO 306/B120 10 13 |
| -- | 82.0 | °C | ISO 306/B50 |
| CLTE | |||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 95.0 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Cylinder Zone 1 Temp. | 180 to 200 | °C | |
| Cylinder Zone 2 Temp. | 180 to 200 | °C | |
| Cylinder Zone 3 Temp. | 180 to 205 | °C | |
| Cylinder Zone 4 Temp. | 180 to 205 | °C | |
| Adapter Temperature | 180 to 205 | °C | |
| Melt Temperature | 190 to 210 | °C | |
| Die Temperature | 185 to 205 | °C | |
| Calibration Temp, First | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mylar® J (142 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Neopor® F 2300 | BASF Corporation | PS (EPS) | Neopor® |
| Daelim Po1y® PP-246H | DAELIM INDUSTRIAL CO., LTD. | PP Impact Copolymer | Daelim Po1y® |
| Kumho EPS GN20 HC | Korea Kumho Petrochemical Co., Ltd. | PS (EPS) | Kumho EPS |
| Moplen RP225N | LyondellBasell Industries | PP Random Copolymer | Moplen |