Grilamid® LV-2A NZ
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9394Zl_Grilamid-LV-2A-NZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilamid® LV-2A NZ is a Polyamide 12 (Nylon 12) material filled with 20% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grilamid® LV-2A NZ are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.12 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 1.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | -- | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4500 | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 85.0 | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | 15 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | -- | 20 | kJ/m² | |
| 23°C | -- | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | -- | 100 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 160 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature | Internal Method | |||
| -- 1 | 90.0 to 120 | -- | °C | |
| -- 2 | 150 | -- | °C | |
| Melting Temperature 3 | 178 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.0E-5 | -- | cm/cm/°C | |
| Transverse | 1.5E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | -- | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 35 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA12, MHR, 22-040, GF20 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics EL-374 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Grivory® GV-5 FWA black 9225 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| HAIPLEN EP100 MF6 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Mafill® CR HT 5344 H | Ravago Group | PP Homopolymer | Mafill® |
| Lifoflex® UV FLAM 50700-2 Anti | Müller Kunststoffe GmbH | SEBS | Lifoflex® |