| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | TRISTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 92zniR_TRISTAR-PC-10FR--8-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRISTAR®PC-10FR-(8) is a polycarbonate (PC) product,. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. TRISTAR®The application areas of PC-10FR-(8) include electrical/electronic applications and wire and cable. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | 75 | % | ASTM D1708 |
| Flexural Modulus (3.17 mm) | 2210 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.17 mm) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.17 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 127 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 137 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 95°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | UL 746 | |
| 3.00 mm | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | UL 746 | |
| 3.00 mm | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 37 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 277 - 291 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 299 - 318 | °C | |
| Nozzle Temperature | 291 - 318 | °C | |
| Processing (Melt) Temp | 302 - 329 | °C | |
| Mold Temperature | 76.7 - 104 | °C | |
| Injection Pressure | 96.5 - 138 | MPa | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Clamp Tonnage | 2.8 - 6.9 | kN/cm² |
| Injection instructions |
|---|
| Injection Speed - Edge Gate: Slow to MediumInjection Speed - Tab Gate: Medium to FastInjection Speed - Tunnel Gate: Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC93-80E | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Yanshan PE 5000S | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| Alpha PVC GW 2038-A-VW1 NAT LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| DOW™ 8818 YL-CF | The Dow Chemical Company | MDPE | DOW™ |
| Hifax TYC 852X GREY | LyondellBasell Industries | TPO (POE) | Hifax |