Devcon Plastic Welder™ II

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	Devcon
Trademark:	Devcon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	92za8t_Devcon-Plastic-Welder-II.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

A 100% reactive, toughened structural acrylic adhesive formulated for bonding difficult-to-bond substrates such as nylon-based alloys, epoxy composites, and modified polyesters.

Intended Use:

Bond: PVC, fiberglass, ABS, PPO, PCBB, Metton®, Lomod®, Valox®, Noryl®, GTX, Minlon®, Nylon, epoxy, RIM urethane, wood, poorly prepared surfaces, and where outdoor weathering or solvent exposure is anticipated.

Features:

Room temperature cure

Bonds dissimilar substrates

Excellent environmental resistance

Minimal surface preparation

Non-sagging formula

Excellent chemical resistance

Excellent impact, peel, and shear resistance

General Information
Features	Solvent resistance Impact resistance, good Adhesiveness Good chemical resistance Good weather resistance
Uses	Bonding Adhesive

Physical	Nominal Value	Unit	Test Method
Specific Volume	1.00	cm³/g
Solid content- by Volume	100	%

Impact	Nominal Value	Unit
Impact Resistance	35.7	kJ/m²

Thermal	Nominal Value	Unit
Service Temperature	-55 - 121	°C

Thermoset	Nominal Value	Unit	Test Method
Work Time (22°C)	15.0 - 20.0	min

Additional Information	Nominal Value	Unit	Test Method
Tensile Shear Adhesion			ASTM D1002
ABS	8.96	MPa	ASTM D1002
GBS	20.7	MPa	ASTM D1002

Physical	Nominal Value	Unit	Test Method
Density ¹	0.998	g/cm³

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	75		ASTM D2240

Mechanical	Nominal Value	Unit
Tensile Elongation (Break)	5.0 - 15	%

Thermoset	Nominal Value	Unit	Test Method
Thermoset Components
Component a	Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0
Component B	Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0
Thermoset Mix Viscosity	56000	cP

Additional Information	Nominal Value	Unit	Test Method
Cured 7 days @ 75°F

Uncured Properties	Nominal Value	Unit	Test Method
Curing Time	24	hr

Note Message
1 .	Mixed

Resin Grade	Manufacturer	Category	Trademark
Sindustris PBT LW5301M	Sincerity Australia Pty Ltd.	PC+PBT	Sindustris PBT
AMTOPP CI25	Inteplast Group	PP, Unspecified	AMTOPP
ASTAMID™ MB3ZUV	Marplex Australia Pty. Ltd.	Nylon 6	ASTAMID™
Cellophane™ XS500	Innovia Films Ltd.	Cellulose, Regenerated	Cellophane™
Chemlon S 133 GVH	Teknor Apex Asia Pacific PTE. LTD.	Nylon 66	Chemlon S