ISPLEN® PP 086 U6E

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	REPSOL
Trademark:	ISPLEN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	92mgUl_ISPLEN-PP-086-U6E.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
ISPLEN® PP 086 U6E is a high melt flow rate polypropylene homopolymer with narrow molecular weight distribution which provides optimum processing in fibre lines of high speed (BCF/CF and spunbond). It includes a specific formulation resistant to "gas fading" coloration, suitable for protecting the polymer during extrusion process and final use. Moreover, it contains additives to increase the resistance to UV radiation. TYPICAL APPLICATIONS Indicated for the extrusion of staple fibre and BCF/CF in lines of high speed. Specially recommended for technical nonwovens in spunbond lines. Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

Message

ISPLEN® PP 086 U6E is a high melt flow rate polypropylene homopolymer with narrow molecular weight distribution which provides optimum processing in fibre lines of high speed (BCF/CF and spunbond). It includes a specific formulation resistant to "gas fading" coloration, suitable for protecting the polymer during extrusion process and final use. Moreover, it contains additives to increase the resistance to UV radiation.

TYPICAL APPLICATIONS

Indicated for the extrusion of staple fibre and BCF/CF in lines of high speed.

Specially recommended for technical nonwovens in spunbond lines.

Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

General Information
Additive	Anti-gas fading
Features	Food Contact Acceptable Gas-fading Resistant Good UV Resistance High Flow Narrow Molecular Weight Distribution
Uses	BCF Multifilaments Nonwovens Spunbond Nonwovens Staple Fibers
Agency Ratings	EU Food Contact, Unspecified Rating
Processing Method	Fiber (Spinning) Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	25	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	36.0	MPa	ISO 527-2
Flexural Modulus	1600	MPa	ISO 178

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	90.0	°C	ISO 75-2/B
Vicat Softening Temperature	153	°C	ISO 306/A

Extrusion	Nominal Value	Unit
Melt Temperature	190 to 250	°C

Resin Grade	Manufacturer	Category	Trademark
Quantum Composites QC-8500	Quantum Composites Inc.	Vinyl Ester	Quantum Composites
Trilliant™ HC HC6200-5001 XR Grey	PolyOne Corporation	Nylon 12	Trilliant™ HC
Gallonprene® GP520-4512	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
Kafrit PEX TA 2125 HD	Kafrit NA Ltd.	XLPE	Kafrit PEX
Sylvin 2934-48 Clear Green 3218	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin