VALOX™ VC130 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 92SkuY_VALOX-VC130-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX™ VC130 resin is a Polybutylene Terephthalate (PBT) material. It is available in Asia Pacific. Primary attribute of VALOX™ VC130 resin: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | Internal Method | ||
| 3.20 mm | 0.10 to 0.20 | % | |
| 6.40 mm | 0.60 to 0.70 | % | |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 167 | MPa | Internal Method |
| Tensile Elongation (Break) | 3.0 | % | Internal Method |
| Flexural Modulus | 17500 | MPa | ASTM D790 |
| Flexural Strength | 239 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 76 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 205 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.55 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® A1400 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Silmar® SIL93BE-1122B | Interplastic Corporation | Polyester, TS | Silmar® |
| THERMOLAST® K TP0LDZ (Series: UV/LD/b) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Axiall PVC 3152 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| HANWHA CLNA-8141SC | Hanwha Chemical | LDPE | HANWHA |