LNP™ LUBRICOMP™ Lexan_WR2210 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 91tQY9_LNP-LUBRICOMP-Lexan-WR2210-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| K (wear) Factor 1 | 85.0 | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 62.1 | MPa | |
| Tensile Elongation 3(Break) | 94 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2390 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 88.3 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.21 | ||
| vs. Steel - Static | 0.17 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 660 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 56.2 | J | ASTM D3763 |
| Tensile Impact Strength 6 | 630 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 127 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 128 | °C | |
| RTI Elec | 100 | °C | UL 746 |
| RTI Imp | 100 | °C | UL 746 |
| RTI Str | 100 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 7 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | xE-10, PV=2000 psi-fpm vs Steel |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Type S |
| 7 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA612 GYEHVN | Shandong Guangyin New Materials Co., Ltd. | Nylon 612 | Shandong PA612 |
| Tool-A-Thane UT-15 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| TORZEN Marathon™ G4000XHL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN Marathon™ |
| Haysite SMC 54500 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| INEOS HDPE K54-05 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |