VALOX™ 357U resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 91nGpm_VALOX-357U-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+PC, UL94V-0/5VA Rated, Impact Modified, Opaque, Unreinforced, UV Stabilized. Applications like bobbins, switches and enclosures. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Specific Volume | 0.750 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.80 to 1.1 | % | |
| Flow 2 | 1.0 to 1.4 | % | |
| Across Flow 3 | 0.90 to 1.3 | % | |
| Across Flow 4 | 1.2 to 1.6 | % | |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Outdoor Suitability | f2 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5 | ASTM D638 | ||
| Yield | 48.3 | MPa | |
| Break | 48.3 | MPa | |
| Tensile Elongation 6(Break) | 110 | % | ASTM D638 |
| Flexural Modulus 7(50.0 mm Span) | 2070 | MPa | ASTM D790 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0 mm Span | 82.7 | MPa | |
| Break, 50.0 mm Span | 82.7 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 530 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D4812 |
| Gardner Impact | ASTM D3029 | ||
| 23°C | 43.4 | J | |
| 23°C 9 | 43.4 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 98.9 | °C | |
| CLTE - Flow | ASTM E831 | ||
| -40 to 40°C | 9.2E-5 | cm/cm/°C | |
| 60 to 138°C | 1.2E-4 | cm/cm/°C | |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.2E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 25 | kV/mm | |
| 3.20 mm, in Air | 19 | kV/mm | |
| 3.20 mm, in Oil | 19 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.20 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.030 | ||
| Arc Resistance 10 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.460 mm | HB | ||
| 0.640 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 0.75 to 2.3 mm |
| 2 . | 2.3 to 4.6 mm |
| 3 . | 0.75 to 2.3 mm |
| 4 . | 2.3 to 4.6 mm |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | Modified |
| 10 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG4 | Shanghai Potomer International Trade Co., Ltd. | PVC, Flexible | Shanghai Potomer |
| TOTAL Polyethylene HDPE 49080 UV | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Niche PA6BK | Niche Polymer, LLC | Nylon 6 | Niche |
| KPOL-NYLON K-NY66/21I | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |
| SABIC® SUPEER™ 8118 | Saudi Basic Industries Corporation (SABIC) | mLLDPE | SABIC® SUPEER™ |