DOWLEX™ 2050B
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 91lX29_DOWLEX-2050B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2050B Polyethylene Resin is a High Density Polyethylene, 1-Octene Copolymer, produced in the SOLUTION™ technology. Main Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.95 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 1.21 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 573 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 726 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 24.1 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 30.1 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 42.2 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 41.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 1100 | % | ASTM D882 |
| TD : Fracture, 51 µm | 1200 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 40 | g | ASTM D1922 |
| TD : 51 µm | 110 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 45 | ASTM D2457 | |
| Haze (50.8 µm) | 23 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Processing Conditions for blown film: Die gap: 70 mil (1.8 mm) Melt temperature: 457°F (236°C) Blow-up Ratio: 2.5:1 Speed: 40 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1499 P X 125056 B | RTP Company | PPSU | RTP |
| Polytron® A50B01 | Polyram Ram-On Industries | Nylon 66 | Polytron® |
| Ultraform® N 2640 Z6 UNC | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| ExxonMobil™ HDPE HD 6605.70 | ExxonMobil Chemical | HDPE Copolymer | ExxonMobil™ HDPE |
| Karina NATURAL PVC COMPOUND 730D25/1-WK | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |