LAPEROS® A430
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | LAPEROS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 91Dz5y_LAPEROS-A430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard, Low wear |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| UL File Number |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | Internal Method | ||
| Across Flow : 1.00 mm | 0.82 | % | |
| Flow : 1.00 mm | -0.020 | % | |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 55 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 175 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 6800 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Flexural Strain | 6.5 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Number | VF2002/BK010P |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 50 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 45 | kV/mm | |
| 3.00 mm | 23 | kV/mm | |
| Dielectric Constant | IEC 60250 | ||
| 1 kHz | 3.50 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 1 kHz | 0.020 | ||
| 1 MHz | 0.020 | ||
| Arc Resistance | 94.0 | sec | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x1 mm; Inj. Pressure 60MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200A GB 20 | RTP Company | Nylon 6 | RTP |
| COSMOPLENE® AW191 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| Karina IVORY PVC COMPOUND ML-850-WK-IS-FLEX (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Huaxia Shenzhou DS600-B | Shandong Huaxia Shenzhou New Material Co., Ltd. | FEP | Huaxia Shenzhou |
| Lupoy® EF1006F | LG Chem Ltd. | PC | Lupoy® |