Staramide PFB42ES
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 90wUGV_Staramide-PFB42ES.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide PFB42ES is Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.44 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 1.9 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 93.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4700 | MPa | ISO 178 |
| Flexural Stress | 145 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 4.4 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 156 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.9E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 9.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STRANOX H-PP40%LFT | Oxford Polymers | PP Homopolymer | STRANOX |
| Mowiflex™ FXT 558 | Kuraray Co., Ltd. | PVOH | Mowiflex™ |
| Tarnamid® T- 27 GF10 MX10 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Kingfa JH720 G30 | Kingfa | PC Alloy | Kingfa |
| Hifax TRC 298X BLACK | LyondellBasell Industries | PP Copolymer | Hifax |