LNP™ THERMOCOMP™ RF007H compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 90Ydnd_LNP-THERMOCOMP-RF007H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF007H is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added feature of this grade is: Healthcare. Also known as: LNP* THERMOCOMP* Compound RF-1007 HC Product reorder name: RF007H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.50 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.73 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11400 | MPa | ASTM D638 |
| -- | 11200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 185 | MPa | ASTM D638 |
| Break | 185 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.5 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 8100 | MPa | ASTM D790 |
| -- 5 | 9450 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 266 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 250 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 249 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 78 | J/m | ASTM D256 |
| 23°C 8 | 8.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 790 | J/m | ASTM D4812 |
| 23°C 9 | 55 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 9.90 | J | ASTM D3763 |
| -- | 3.60 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 258 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 252 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 245 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7600 H | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| NuSil R-1140 | NuSil Technology | Silicone | NuSil |
| APEX® 6500-80 | Teknor Apex Company | PVC, Flexible | APEX® |
| Axiall PVC 15900 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| PALGLAS® R 08 | pal plast GmbH | Acrylic (PMMA) | PALGLAS® |