| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® ETP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 90Kq8G_Alathon-ETP-H4250.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON H4250 is a high-flow "freezer" grade resin that exhibits enhanced cold temperature impact performance, enhanced processing and thermal stability, with good color and organoleptic properties. Typical applications are rigid food containers such as four, five and six-quart ice cream containers that are produced at high speeds in fast cycling multi-cavity stack molds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.942 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.62 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 50 | g/10 min | ASTM D1238 |
| Spiral Flow | 43.7 | cm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -- 1 | 943 | MPa | |
| 1% Secant 2 | 692 | MPa | |
| Tensile Strength 3(Break) | 21.1 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 12 | % | ASTM D638 |
| Flexural Modulus 5 | ASTM D790 | ||
| -- | 941 | MPa | |
| 1% Secant | 826 | MPa | |
| 2% Secant | 704 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 35 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 59.4 | °C | ASTM D648 |
| Vicat Softening Temperature | 116 | °C | ASTM D1525 |
| Peak Melting Temperature | 124 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 113 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | Type IV, 50 mm/min |
| 5 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® MRGF25/15 42H-BKJA6A | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| TOTAL Polypropylene PPR 3727W | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Adell Polyamide AO-16 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| DINALON® A1X25 G33MI H | Grupo Repol | Nylon 66 | DINALON® |
| MAJORIS PBT 9237 50 FV BLACK 8229 | AD majoris | PBT | MAJORIS |