Characteristics:
Applications:
|
General Information | |
---|---|
Features |
|
Uses |
|
Appearance |
|
Physical | Nominal Value | Unit | |
---|---|---|---|
Molding Shrinkage - Flow | < 1.3 | % | |
Water Absorption (Equilibrium) | < 0.25 | % | |
Acid Value | < 26.00 | mg KOH/g | |
Gardner Color | < 1.50 |
Thermal | Nominal Value | Unit | |
---|---|---|---|
Heat Deflection Temperature | > 60 | °C |
Hardness | Nominal Value | Unit | |
---|---|---|---|
Barcol Hardness | > 40 |
Mechanical | Nominal Value | Unit | |
---|---|---|---|
Tensile Strength | > 60.0 | MPa | |
Tensile Elongation (Break) | > 4.0 | % | |
Flexural Strength | > 115 | MPa |
Thermal | Nominal Value | Unit | |
---|---|---|---|
Peak Melting Temperature | < 190 | °C |
Uncured Properties | Nominal Value | Unit | |
---|---|---|---|
Solids Content | 60 to 64 | % | |
Viscosity (25°C) | 0.38 to 0.48 | Pa·s | |
Curing Time | 0.13 to 0.27 | hr | |
Gel Time 1 | 11 to 18 | min |
Note Message | |
---|---|
1 . | Curing condition with 0.5% Co (1%) and 2% MEKP (50%) |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Telcar® OBC 2318D | Teknor Apex Company | TPE | Telcar® |
Talcoprene® 1522SMT NERO | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
DINALON® B1S25 G15 | Grupo Repol | Nylon 6 | DINALON® |
Lanufene LLF 182H | Ras Lanuf Oil & Gas Processing Company (RASCO) | LLDPE | Lanufene |
Iupilon® GSH2020TR 9005 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |