LNP™ THERMOCOMP™ JF004L compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8zWT6s_LNP-THERMOCOMP-JF004L-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF004L is a compound is based on Polyethersulfone containing 20% Glass Fiber. Characteristics of this grade is: Low Extractible Also known as: LNP* THERMOCOMP* Compound JF-1004 LE Product reorder name: JF004L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.54 | g/cm³ | |
| -- | 1.53 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.60 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.37 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.55 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6360 | MPa | ASTM D638 |
| -- | 6650 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 98.9 | MPa | ASTM D638 |
| Yield | 94.4 | MPa | ISO 527-2/5 |
| Break 3 | 98.6 | MPa | ASTM D638 |
| Break | 93.6 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.7 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2/5 |
| Break 5 | 2.9 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6300 | MPa | ASTM D790 |
| -- 7 | 6310 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 149 | MPa | ISO 178 |
| -- | 149 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 152 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 50 | J/m | ASTM D256 |
| 23°C 10 | 5.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 560 | J/m | ASTM D4812 |
| 23°C 11 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.0 | J | ASTM D3763 |
| -- | 2.64 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 216 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 216 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 211 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 210 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol H-622 | Shanghai Suptech Engineering Plastics Co. Ltd. | TPO (POE) | Supol |
| Geon™ CPVC LC510 | PolyOne Corporation | CPVC | Geon™ CPVC |
| ELASTOSIL® RD 6600 F | Wacker Chemie AG | Silicone | ELASTOSIL® RD |
| Laramid G/30-V0HF1 | LATI S.p.A. | PPA | Laramid |
| LNP™ LUBRICOMP™ VN001 compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ LUBRICOMP™ |