Order Products : sales@su-jiao.com
Bio-Flex® F 6611
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8zNVb2_Bio-Flex-F-6611.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bio-Flex® F 6611Biodegradable compound for thermoforming. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 - 3.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.50 - 3.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2740 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 47.0 | MPa | ISO 527-2 |
| Fracture | 19.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 22 | % | ISO 527-2 |
| Flexural Modulus | 2840 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 63.0 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | 5.2 | % | ISO 527 |
| Flexural Strain at Break | No Break | % | ISO 178 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Calendar Temperature Profile | 20 - 50 | °C |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.2 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 150 - 170 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 150 | °C | |
| Middle Temperature | 160 | °C | |
| Front Temperature | 175 | °C | |
| Nozzle Temperature | 190 | °C | |
| Mold Temperature | 25.0 - 40.0 | °C |
| Injection instructions |
|---|
| Holding pressure level: 40 - 60%Melt cushion (of volume): < 10%Cooling time: 15 secmax. Dwell time: 300 sec |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 175 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 185 | °C | |
| Adapter Temperature | 195 | °C | |
| Die Temperature | 195 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3101-10 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| ALTECH® PA6 A 2015/210 GF15 IM | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Jiangsu Sinarise EI9000X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| K-Bin Rigid PVC KB-6108 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| LUVOCOM® 1850-8710 | Lehmann & Voss & Co. | PBT | LUVOCOM® |