Clearflex® FG 336
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ygR61_Clearflex-FG-336.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FG 336 is a hexene copolymer linear low density polyethylene (C6-LLDPE), additivated with antioxidant, slip agent, antiblocking agent and processing aid, suitable for blown film extrusion. Films obtained from Clearflex FG 336 show high rigidity together with optimum Elmendorf tear and impact resistance. Main Application Clearflex FG 336 is recommended for shipping sacks, where the perfect balance between additivation (in terms of slip and antiblocking) and mechanical performances leads to the manufacture of a tough and easy peelable film. Moreover, for its sealing characteristics, together with low temperature mechanical resistance, Clearflex FG 336 is suggested for the production of freezer bags, either in coextrusion and in blend with LDPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.11 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 200 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 13.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 45.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 36.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 550 | % | |
| TD : Break, 25 µm, Blown Film | 740 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 82.0 | kN/m | |
| TD : 25.0 µm | 250.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 110 | °C | ISO 306/A |
| Melting Temperature | 127 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 54 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 13 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G2030HR-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| NORYL™ WCA901 resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |
| LG PS 460AF | LG Chem Ltd. | PS (HIPS) | LG PS |
| LUVOCOM® 1-8719/RD | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| PALFORM® R C 09 | pal plast GmbH | Acetal (POM) Copolymer | PALFORM® |