DOWLEX™ 2285G
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8xg3Ov_DOWLEX2285G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX 2285G is a blown film extrusion linear low density polyethylene resin grade suitable for high toughness film applications. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 4.18 | J | Internal method |
| Film Puncture Force | 53.4 | N | Internal method |
| Film Puncture Resistance | 20.5 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 87.9 | J/cm³ | ASTM D882 |
| TD | 112 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 188 | MPa | ASTM D882 |
| 2% secant, MD | 171 | MPa | ASTM D882 |
| 1% secant, TD | 208 | MPa | ASTM D882 |
| 2% secant, TD | 183 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.1 | MPa | ASTM D882 |
| TD : Yield | 11.4 | MPa | ASTM D882 |
| MD : Fracture | 44.8 | MPa | ASTM D882 |
| TD : Fracture | 42.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 450 | % | ASTM D882 |
| TD : Fracture | 640 | % | ASTM D882 |
| Dart Drop Impact | 620 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 380 | g | ASTM D1922 |
| TD | 660 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Melting Temperature | 119 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 41 | ASTM D2457 | |
| Haze | 19 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 224 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5 in. Screw Type: DSB II Die Gap: 70mil Melt Temperature: 436°F Output: 12 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 38.9 rpm Frost Line Height: 40 in. |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-551U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Badadur® PBT/PC FR V0 | Bada AG | PC+PBT | Badadur® |
| ALCOM® PC 740/4 CC1122-05LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| CHEMIGUM® P8D | Omnova Solutions Inc. | NBR | CHEMIGUM® |
| LNP™ LUBRICOMP™ Noryl_SPN422L compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |