LEXAN™ 503R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8xRYQb_LEXAN-503R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. Internal mold release. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Specific Volume | 0.802 | cm³/g | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | Internal Method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.12 | % | |
| Equilibrium, 23°C | 0.31 | % | |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 85 | ||
| R-Scale | 124 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 66.2 | MPa | |
| Break | 55.2 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 8.0 | % | |
| Break | 15 | % | |
| Flexural Modulus 3(50.0 mm Span) | 3450 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 103 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 11.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 102 | J | ASTM D3029 |
| Tensile Impact Strength 5 | 158 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 146 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 142 | °C | |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 6 |
| CLTE - Flow (-40 to 95°C) | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1210 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.10 | ||
| 60 Hz | 3.10 | ||
| 1 MHz | 3.05 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 8.0E-4 | ||
| 60 Hz | 8.0E-4 | ||
| 1 MHz | 7.5E-3 | ||
| Arc Resistance 7 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.52 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Oxygen Index | 36 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 288 to 310 | °C | |
| Middle Temperature | 299 to 321 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 304 to 327 | °C | |
| Processing (Melt) Temp | 310 to 332 | °C | |
| Mold Temperature | 82.0 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Type S |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| 7 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Gallonprene® GP520-6512 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| ENFLEX V1090A BLK UV | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
| Kotex K-50UVR | Kotec Corporation | PC | Kotex |
| Hylon® N1000STHLUV2HF | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| PermaStat® 1200 T-70A | RTP Company | TPU-Polyether | PermaStat® |