Order Products : sales@su-jiao.com
OnForce™ LFT NY-30LGF/000 HS NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnForce™ LFT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8x4rR8_OnForce-LFT-NY-30LGF-000-HS-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8350 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 8200 | MPa | ISO 178 |
| Flexural Stress | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 85 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 90.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 5.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tufel® II 94606 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| TRISTAR® PC-30GF | Polymer Technology and Services, LLC | PC | TRISTAR® |
| ADPOLY CM-1120H | Lotte Chemical Corporation | PP, Unspecified | ADPOLY |
| Sylvin 8486-75LG Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Durethan® AKV 30 HR H2.0 900116 | LANXESS GmbH | Nylon 66 | Durethan® |