Carboprene® 1040AV NATURALE
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Carboprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8wBVND_Carboprene-1040AV-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer, 40% calcium carbonate filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 1.1 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Ash Content | 40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 23.0 | MPa | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Dielectric Constant (1 kHz) | 2.50 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 230 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE J 326 V30 | ADDIPLAST | PP Copolymer | ADDILENE |
| Cheng Yu FRCV150 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| Hanwha Total PP HJ730 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Alpha PVC 3006-60 | Mexichem Specialty Compounds Inc. | PVC, Flexible | Alpha PVC |
| Kepital® F20-03 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |