TRANSMARE® 35HGF30-0.001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8vxMRn_TRANSMARE-35HGF30-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 35HGF30-0.001 is a 30% chemically coupled glass fiber reinforced polypropylene homopolymer. It combines good impact properties with a high stiffness, and very good flow properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 6470 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 4.00 mm) | 90.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus | 5450 | MPa | ISO 178 |
| Flexural Stress | 125 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 7.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C | 33 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C | 35 | kJ/m² | |
| 23°C | 44 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 156 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 133 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 162 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 230 | °C | |
| Front Temperature | 240 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Slow-Moderate |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3830 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Vikalloy P40 | Viking Polymers, LLC | PMMA+PVC | Vikalloy |
| Etinox® EK-8780 | Ercros, S.A. | PVC, Flexible | Etinox® |
| Geon™ Vinyl Packaging 161J-1 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Packaging |
| LubriOne™ PC-000/5T-2S NC704 | PolyOne Corporation | PC | LubriOne™ |