MAJORIS DE 271
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8vsCTa_MAJORIS-DE-271.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DE 271 is a 25% mineral filled, polypropylene compound, elastomer modified intended for injection moulding. DE 271 is a material with excellent impact/stiffness ratio. The product is UV and heat stabilised. The product is available in natural and black (DE 271 BLACK 8229) but other colours can be provided on request. APPLICATION Automotive parts:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C, Injection Molded) | 20.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1(23°C, Injection Molded) | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, injection molding | 2.5 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | 33 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | 100 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 112 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ISO 306/A |
| -- | 59.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Fogging, DIN 75201, 100°C/3h: 88%Fogging, DIN 75201, 100°C/16h: 0.4mgEmission, VDA 277: 27 µ gC/g |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Hold-on Pressure: 50 - 70% of the injection pressureSpeed RPM: slow to medium |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2665 MAS071 | Covestro - Polycarbonates | PC | Makrolon® |
| Prime Polypro™ J715M | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| DENKA STYROL MW-1-321 | Denka Company Limited | PS (GPPS) | DENKA STYROL |
| Fainplast PVC RST 0413 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Latishield 87/28-10A | LATI S.p.A. | PC | Latishield |