FORMULA P COMP 5220
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8vUyLV_FORMULA-P-COMP-5220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene with 20% talc reinforcement with a good flow and good heat resistance. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 - 1.3 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 26.0 | MPa | ISO 527-2 |
| Fracture | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 | % | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 49.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 85.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 26 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 240 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TB130L | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| Bergadur™ PB40 G10 NC007 | PolyOne Corporation | PBT | Bergadur™ |
| 3M™ Dyneon™ PTFE Compound FM 2370081 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| NORYL™ NH6010B resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| ULTEM™ 2200R resin | SABIC Innovative Plastics | PEI | ULTEM™ |