Ferro PP LPP35BF54HB-WH
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8uyoxU_Ferro-PP-LPP35BF54HB-WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP LPP35BF54HB-WH is a Polypropylene material filled with 35% calcium carbonate. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 24.8 | MPa | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 42.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Impact | 6.78 | J | ASTM D3029 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 202 to 204 | °C | |
| Middle Temperature | 204 to 210 | °C | |
| Front Temperature | 210 to 213 | °C | |
| Nozzle Temperature | 213 to 218 | °C | |
| Mold Temperature | 43.3 to 51.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinelec CCB6825 | Teknor Apex Asia Pacific PTE. LTD. | PS (Specialty) | Sinelec |
| Wellamid® FRGS25-66-NBK3 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Baytec® 352 (76A) | Covestro - PUR | TSU | Baytec® |
| LACTEL® 25:75 DL-PLCL | DURECT Corporation | PCL | LACTEL® |
| PALBLEND® R 65 | pal plast GmbH | PC+ABS | PALBLEND® |