Order Products : sales@su-jiao.com
DENISTAT A 00U 05
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Vamp Tech |
| Trademark: | DENISTAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8uQgVQ_DENISTAT-A-00U-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP copo 40% glass fiber reinforced, surface resistivity 10^3 ohm. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 | % | |
| Across Flow | 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 4.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 1 |
| RTI Elec | 70.0 | °C | UL 746 |
| RTI Imp | 70.0 | °C | UL 746 |
| RTI Str | 70.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 | °C | |
| Mold Temperature | 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Durethan® B 35 F KA 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| HiFill® PA6/6 IM L UV | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Karina BLACK PVC COMPOUND 670D48/ 1-BY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ IF006L compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ HF008 compound | SABIC Innovative Plastics | Nylon 11 | LNP™ THERMOCOMP™ |