Vitaster® UR33OR6654
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Vitaster® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8uKHR4_Vitaster-UR33OR6654.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vitaster® UR33OR6654 is a Polybutylene Terephthalate (PBT) product filled with 15% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.22 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 125 | MPa | ISO 178 |
| Break | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 35 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 215 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 1218, ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 29 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 20 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP RA2E70 | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| TYRIL™ 867 E | Trinseo | SAN | TYRIL™ |
| APEX® 77-W385-A | Teknor Apex Company | PVC, Flexible | APEX® |
| POLIFAIN 6020 | Fainplast Compounds S.r.l | PVC, Unspecified | POLIFAIN |
| LNP™ LUBRICOMP™ LCL36E compound | SABIC Innovative Plastics Europe | PEEK | LNP™ LUBRICOMP™ |