INSTRUC PPMIN20
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8srxxB_INSTRUC-PPMIN20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% MINERAL FILLED POLYPROPYLENE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.4 to 1.8 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 31.0 | MPa | ASTM D638 |
| Flexural Modulus | 2240 | MPa | ASTM D790 |
| Flexural Strength | 46.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1200 to 1400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 62.8 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+17 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 193 to 227 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BCC Resins BC 8002 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| Grilon® AG-35 | EMS-GRIVORY | Nylon 66 | Grilon® |
| Infino GP-8300G | SAMSUNG SDI CO., LTD. | PPE | Infino |
| DOWLEX™ 6000G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Delene 1180 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |